Recommended special PVC glue suitable for all repairs to the TAMI dog crate.
These tubes fit into the TAMI repair cartridge and can be safely stored there.
This adhesive offers an optimal adhesive solution. The solvent mixture contained dissolves the plastic PVC surface. This leads to a so-called solvent weld bonding of the two PVC parts to be joined. The additional formula components included improve dissolving and enable optimized joint filling.
The adhesive has a processing time of 10 – 30 seconds. The initial strength is reached after just a few minutes. Since this involves “cold welding”, the adhesive parts must be firmly fixed until the initial strength is achieved. Attention: Air and water temperatures below +15 °C can lead to reduced bonding results!
Also preferably suitable for gluing: standup paddle boards, inflatable boats, soft PVC films, vinyl to each other and to other materials, textiles, wood, paper/cardboard, artificial leather
Color: colorless, transparent
Capacity: 2x 38g tube
Shelf life: At least 3 years when stored in a cool, dry place in the original sealed container.
Application
Bonding of soft PVC films to each other, as well as to hard PVC and other materials.
Application examples
TAMI inflatable dog boxes, standup paddle boards (SUP), inflatable boats, swimming pool liners, pond liners and vehicle tarpaulins made of soft PVC. For regluing and repair work, PVC pipes.
Processing instructions/product data
Base Polymer
Viscosity (+23 °C) approx. 550 mPas
Solids content approx. 27%
Density 1.0 g/cm3
Color colorless, transparent
Wet bonding time approx. 10 to 30 seconds (one-sided application) max. 1 minute (two-sided Application)
Application type on one and both sides
Processing temperature +15 °C to +25 °C
Consumption 150 – 250 g/m2
Cleaning Hardened adhesive can only be removed mechanically.
Permissible storage time At least 3 years when stored in a cool, dry place in the original sealed container.
Preferred storage temperature +10 °C to +25 °C
Cold behavior
Not sensitive to frost. Thickening at lower temperatures. Fully usable after heating to processing temperature.